Título: Ceramic repair: influence of chemical and mechanical surface conditioning on adhesion to zirconia
Autor: Barragan, Gonçalo
Chasqueira, Filipa
Oliveira, Sofia Arantes
Palavras-chave: Zirconia
Shear strength
Dental restoration repair
Primer
Air abrasion
Data: 2014
Citação: Barragan G, Chasqueira F, Oliveira SA, et al. Ceramic repair: influence of chemical and mechanical surface conditioning on adhesion to zirconia. Oral Health Dent Manag. 2014;13(2):155-158.
Resumo: Aims: To evaluate the influence of mechanical surface treatment and chemical primer application on the composite shear bond strength to zirconia. Methods: Eighty blocks of Lava Frame Zirconia were randomly assigned to the experimental groups, according to the several possible combinations between mechanical (untreated/aluminum oxide sandblast) and chemical treatment (no primer/Monobond Plus/Experimental Zirkon-Primer/Z-Prime Plus) (n=10). Adhesive system and composite resin were then applied, and samples were thermal cycled (5ºC-55ºC, 500 cycles). Shear bond strength tests and failure mode analysis were performed. SBS data were analyzed by two-way ANOVA, followed by Student-Newman-Keuls post-hoc tests, and failure mode by Kruskal-Wallis and Mann-Whitney tests (p<0.05). Results: Shear bond strength mean values ranged from 6.9 to 23.2 MPa. Surface treatment with aluminum oxide sandblasting allowed a statistically significant increase (p<0.05) in bond strength values. The group treated with Z-Prime Plus achieved (p<0.05) higher bond strength results than the other chemical treatments. Conclusions: The surface mechanical treatment almost doubled the bond strength values. Z-Primer Plus have enhanced bond strength values of composite to zirconia.
Peer review: yes
URI: http://hdl.handle.net/10451/35301
Aparece nas colecções:FMD - Artigos em Revistas Internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
WU190_OLIs C_AI_2014.pdf363,51 kBAdobe PDFVer/Abrir    Acesso Restrito. Solicitar cópia ao autor!


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.